Investigation Of Boron Spin On Dopant On SOI Wafer

Bahaudin, Aishah Shamimi (2022) Investigation Of Boron Spin On Dopant On SOI Wafer. Project Report. Universiti Sains Malaysia, Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral. (Submitted)

[img]
Preview
PDF
Download (715kB) | Preview

Abstract

In this research, works were focused on the doping technique of p-type SOI wafers by using thermal diffusion process. The aim of this research was to prepare doped of p-type SOI wafer by SOD with boron dopant. This method is used to provide an impurity source for SOI wafer. The dopant was first spread into the substrate via SOD and then diffused by a thermal diffusion process at 700˚C, 800˚C, 800˚C and 1000˚C. Various characterization instruments were used to investigate the properties of SOD technique on doping. Four-point probe was done to obtain the resistivity and sheet resistance of doped SOI wafer. The resistivity was decrease as well as sheet resistance with increasing the diffusion time and temperature. The dopant concentration was increased as the diffusion time and temperature increased. The surface roughness of doped SOI wafer for 120 minutes of diffusion were analyse using AFM. From the analysis, RMS values were obtained to describe the surface roughness after thermal diffusion. From result, the surface roughness around 30.0 nm to 80.0 nm were obtained with increasing diffusion temperature. However, at 900˚C, the RMS value was decrease due to etchant effect. To conclude, the selected thermal diffusion temperature is at 900˚C would lead to the best result SOD as it has high concentration, high carrier density, lower mobility and lowest surface roughness which the value of 7.17E+15cm−3, 8.506E+14 1/cm2, 4.885E+2 cm2/vs and 34.92nm respectively.

Item Type: Monograph (Project Report)
Subjects: T Technology
T Technology > TN Mining Engineering. Metallurgy
Divisions: Kampus Kejuruteraan (Engineering Campus) > Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral (School of Material & Mineral Resource Engineering) > Monograph
Depositing User: Mr Engku Shahidil Engku Ab Rahman
Date Deposited: 19 Jan 2023 09:00
Last Modified: 19 Jan 2023 09:00
URI: http://eprints.usm.my/id/eprint/56433

Actions (login required)

View Item View Item
Share