Catalytic Hydrogenation Of Co2 Over Cuznosba-15 Catalysts For Production Of Methanol

Asri, Sahrizul Aman (2016) Catalytic Hydrogenation Of Co2 Over Cuznosba-15 Catalysts For Production Of Methanol. Masters thesis, Universiti Sains Malaysia.

Preview

PDF - Submitted Version Download (395kB) | Preview

Abstract

Isu-isu pemanasan global telah menjadi kebimbangan utama di seluruh dunia. Punca utama pemanasan global adalah disebabkan oleh jumlah gas rumah hijau yang semakin meningkat di atmosfera terutamanya gas karbon dioksida (CO2). Penghasilan metanol dari CO2 dianggap sebagai alternatif kepada kaedah pemencilan CO2 secara geologi dan lautan yang mahal. Pemangkin Cu/ZnO dilaporkan menjadi aktif untuk pengeluaran metanol dari penghidrogenan CO2. Untuk kajian ini, objektif utama adalah untuk menghasilkan mangkin Cu/ZnO/SBA-15 beraktiviti tinggi untuk penghidrogenan CO2 bagi penghasilan metanol. SBA-15 telah disintesis menggunakan kaedah konvensional tanpa melalui langkah hidroterma dan logam Cu/ZnO telah dimuatkan pada sokongan menggunakan kaedah pemendapan bersama. Pencirian telah dijalankan ke atas SBA-15 dan pemangkin disintesis Cu / ZnO / SBA-15. SBA-15 yang disediakan mempunyai morfologi seperti serat dengan luas permukaan BET, luas liang micro, luas liang meso dan isipadu liang 716,98 m2/g, 188,32 m2/g, 528 m2/g dan 0.70 cm3/g. Cu/ZnO/SBA-15 dengan pada nisbah Cu: ZnO: SBA-15 3: 4: 6 (23.1% berat Cu) telah dipilih sebagai pemangkin terbaik untuk kajian ini dan digunakan untuk kajian proses. Keadaan reaksi terbaik adalah pada jumlah halaju gas setiap jam (GHSV) 3600 h-1, suhu 543 K dan tekanan 5.0 MPa dengan penukaran CO2 pada 22% dengan hasil metanol 17.0%. Tenaga pengaktifan bagi pengeluaran metanol dari penghidrogenan CO2 telah ditentukan daripada Arrhenius plot dan tenaga pengaktifan yang dianggarkan adalah 43 kJ / mol. ________________________________________________________________________________________________________________________ Global warming issues had been widely become main concern worldwide. The main cause of the global warming is due to increasing amount of the greenhouse gases in the atmosphere especially carbon dioxide (CO2) gas. The production of methanol from CO2 considered as the alternative to the costly geological and oceanic CO2 sequestration. Cu/ZnO based catalyst had been reported to be active for the production of the methanol from CO2 hydrogenation. For this study, the main objective was to synthesized high activity of Cu/ZnO/SBA-15 for hydrogenation of CO2 to produce methanol. SBA-15 support was synthesized using conventional method without the hydrothermal aging and the Cu/ZnO metal was loaded on the support using deposition co-precipitation method. The characterizations been carried out on the synthesized SBA-15 and catalyst Cu/ZnO/SBA-15. The prepared SBA-15 having fibre like morphology with BET surface area, micropore area, mesopore area and pore volume of 716.98 m2/g, 188.32 m2/g, 528 m2/g and 0.70 cm3/g, respectively. The Cu/ZnO/SBA-15 with Cu:ZnO:SBA-15 ratio 3:4:6 (23.1 wt% Cu) was selected as the best catalyst for this studies and used for the process studies. The best reaction condition was at total gas hourly space velocity (GHSV) of 3600 h-1, temperature 543 K and pressure 5.0 MPa with conversion of CO2 at 22% with methanol yield of 17.0%. The activation energy for the production of methanol from CO2 hydrogenation was determined from Arrhenius plot and the estimated activation energy was 43 kJ/mol.

Item Type:	Thesis (Masters)
Additional Information:	Full text is available at http://irplus.eng.usm.my:8080/ir_plus/institutionalPublicationPublicView.action?institutionalItemId=3076
Subjects:	T Technology T Technology > TP Chemical Technology > TP1-1185 Chemical technology
Divisions:	Kampus Kejuruteraan (Engineering Campus) > Pusat Pengajian Kejuruteraan Kimia (School of Chemical Engineering) > Thesis
Depositing User:	Mr Mohd Jasnizam Mohd Salleh
Date Deposited:	29 Aug 2018 08:10
Last Modified:	29 Aug 2018 08:10
URI:	http://eprints.usm.my/id/eprint/41584

Actions (login required)

View Item