Synthesis And Characterization Of Low Bandgap Nanocrystalline T-Zirconia [TA418.9.N35 N692 2007 f rb].

Prastomo, Niki (2007) Synthesis And Characterization Of Low Bandgap Nanocrystalline T-Zirconia [TA418.9.N35 N692 2007 f rb]. Masters thesis, Universiti Sains Malaysia.

[img]
Preview
 PDF
Download (369kB) | Preview

Abstract

Serbuk nanohablur t-ZrO2 disintesis melalui kaedah kimia untuk mencari kemungkinan jika dop elektronik akan meningkatkan konduktiviti elektronik oksida. Y3+ ditambah sebagai penstabil untuk mengekalkan fasa t-ZrO2 manakala Nb5+ dimasukkan untuk dop elektronik. Nanocrystal t-ZrO2 powders were synthesized through a chemical route to seek a possibility if electronic doping would improve the electronics conductivity of the oxide. Y3+ was added as a stabilizer to retain tetragonal phase ZrO2 whereas Nb5+ was added for electronics doping.

Item Type: Thesis (Masters)
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA401-492 Materials of engineering and construction. Mechanics of materials
Divisions: Kampus Kejuruteraan (Engineering Campus) > Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral (School of Material & Mineral Resource Engineering) > Thesis
Depositing User: Mr Erwan Roslan
Date Deposited: 23 Apr 2009 07:22
Last Modified: 15 May 2017 08:05
URI: http://eprints.usm.my/id/eprint/9488

Actions (login required)

View Item View Item
USM Repository is powered by EPrints 3 which is developed by the School of Electronics and Computer Science at the University of Southampton. More information and software credits.
Share