Othman, Rusli (1986) High-Strength Interstitial Alloys. PhD thesis, Universiti Sains Malaysia.
|
PDF
Download (23MB) | Preview |
Abstract
During nitriding of Mo powder. surface hardening of the sample due to the formation of b-MoN was observed. The sintered layer of S-MoN reduced the passage of nitrogen to the interior of the sample being completely nitrided and hence prevented it from only a thin layer of Mo powder was therefore completely nitrided to b-MoN in one run and so large scale production of b-MoN by this method is not possible.
| Item Type: | Thesis (PhD) |
|---|---|
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA401-492 Materials of engineering and construction. Mechanics of materials |
| Divisions: | Kampus Kejuruteraan (Engineering Campus) > Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral (School of Material & Mineral Resource Engineering) > Thesis |
| Depositing User: | Mr Aizat Asmawi Abdul Rahim |
| Date Deposited: | 05 May 2025 08:34 |
| Last Modified: | 05 May 2025 08:34 |
| URI: | http://eprints.usm.my/id/eprint/62179 |
Actions (login required)
 |
View Item |