Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement

Syedsalim, Sharifah Aishah (2014) Nio Modification Using Zr4+ And Ca2+ For Dielectric Improvement. Masters thesis, Perpustakaan Hamzah Sendut.

[img]
Preview
PDF
Download (28MB) | Preview

Abstract

In this research, the effect of Zirconium ions (Zr4+) and Calcium ions (Ca2+) dopant on NiO was investigated. The electroceramic of Ni(l_;c)ZrxO, Ni(l_x)CaxO and Nio.9SZrO.o2CaO.OI was prepared by using solid state reaction method. Three main raw materials ofNiO, Zr02 and CaO were mixed for 24 hours, then were calcined at 1000°C. Ni(l_x)Zr.

Item Type: Thesis (Masters)
Subjects: T Technology > TN Mining Engineering. Metallurgy > TN1-997 Mining engineering. Metallurgy
Divisions: Kampus Kejuruteraan (Engineering Campus) > Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral (School of Material & Mineral Resource Engineering) > Thesis
Depositing User: Mr Hasmizar Mansor
Date Deposited: 11 Sep 2024 02:19
Last Modified: 11 Sep 2024 02:20
URI: http://eprints.usm.my/id/eprint/61091

Actions (login required)

View Item View Item
Share