Chromaticity Study Of La2O3-PVA Phosphor Nanofibers Prepared By Electrospinning Process For Uv Light Down Conversion For White Light Emitting Diode

Wahab, Hasma A. and Hassan, Z. and Ahmed, Naser M. (2020) Chromaticity Study Of La2O3-PVA Phosphor Nanofibers Prepared By Electrospinning Process For Uv Light Down Conversion For White Light Emitting Diode. In: 5th Meeting of Malaysia Nitrides Research Group (MNRG 2020).

[img]
Preview
PDF
Download (231kB) | Preview

Abstract

Lanthanum oxide-polyvinyl alcohol (La2O3-PVA) phosphor nanofibers had been prepared using electrospinning process with four different thicknesses (2.0, 6.0, 13.0 and 59.0 μm) and each sample with the same thickness was investigated with different annealing temperatures (100, 200, 300 and 500 ℃). The phosphor was used for light downconversion of UV light (365 nm) for fabrication of white light emitting diode (WLED). The resulting phosphor nanofibers were observed and analyzed by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and ultraviolet-visible (UV-Vis) spectroscopy. The chromaticity coordinates (CIE) and correlated color temperature (CCT) of the WLED were measured with different thickness and temperature of phosphor nanofibers by using HPC-2 lightsource colorimeter with applied voltage and current of 8.4 V and 0.14 A respectively. The comparison showed that lanthanum oxide-polyvinyl alcohol (La2O3-PVA) phosphor nanofibers exhibited CIE values of 0.3575, 0.4308 and CCT of 4835 K. The annealing temperature and thickness of phosphor were confirmed to be major factors that control the intensity of white light emitted from the sample.

Item Type: Conference or Workshop Item (Paper)
Subjects: Q Science > QC Physics > QC1-999 Physics
Divisions: Institut Penyelidikan dan Teknologi Nano Optoelektronik (Institute of Nano Optoelectronics Research and Technology (INOR)) > Conference or Workshop Item
Pusat Pengajian Sains Fizik (School of Physics) > Conference or Workshop Item
Depositing User: Mr Aizat Asmawi Abdul Rahim
Date Deposited: 21 Apr 2021 01:49
Last Modified: 21 Apr 2021 01:49
URI: http://eprints.usm.my/id/eprint/48961

Actions (login required)

View Item View Item
Share