Effects Of Dry Oxidation Treaments On The Characteristics Of Gallium Oxide Thin Films Prepared Using Sol-Gel Spin Coating Method

Kwok, Eunice and Hamid, Maizatul Akman Ab and TianKun, Wang and Sha, Shiong Ng (2020) Effects Of Dry Oxidation Treaments On The Characteristics Of Gallium Oxide Thin Films Prepared Using Sol-Gel Spin Coating Method. In: 5th Meeting of Malaysia Nitrides Research Group (MNRG 2020).

[img]
Preview
PDF
Download (230kB) | Preview

Abstract

In this paper, gallium oxide (Ga2O3) thin films were grown on silicon (Si) substrate using a relatively simple and low-cost sol-gel spin coating method followed dry oxidation process. Two series of dry oxidation experiments were conducted, i.e., (i) annealing at different oxygen flow rates (i.e., from 2 L/min – 5 L/min) under 1100°C, and (ii) annealing at oxygen flow rate of 5 L/min under different temperatures (i.e., from 800°C to 1100°C). The effects of the oxygen gas flow rates under different temperatures on the structural, surface morphology, and optical properties of the deposited films were investigated. All results revealed that crystalline Ga2O3 layers were formed. From the X-ray diffraction results, all deposited films exhibit two prominent diffraction peaks corresponding to the Ga2O3 (1 ̅10) and (002). The annealing at different temperatures experiments showed that the surface roughness and the grains size increased as the temperature increases from 800°C to 1100°C. The optical band gap energy of the deposited films was extracted from the Ultraviolet-violet transmission spectra. This obtained energy bandgap is within the ranges of 4.69 – 4.83 eV, i.e., in reasonable agreement with the reported values. In summary, all the results showed that polycrystalline Ga2O3thin films were able to be grown on p-Si (100) substrate through the proposed methodology. While the best conditions for the dry oxidation process are at the oxygen flowrate of 5 L/min at temperature of 1100o C.

Item Type: Conference or Workshop Item (Paper)
Subjects: Q Science > QC Physics > QC1-999 Physics
Divisions: Institut Penyelidikan dan Teknologi Nano Optoelektronik (Institute of Nano Optoelectronics Research and Technology (INOR)) > Conference or Workshop Item
Depositing User: Mr Aizat Asmawi Abdul Rahim
Date Deposited: 19 Apr 2021 03:25
Last Modified: 19 Apr 2021 03:25
URI: http://eprints.usm.my/id/eprint/48922

Actions (login required)

View Item View Item
Share