Isa, Nurul Atikah Mohd and Ng, Sha Shiong and Hassan, Zainuriah
(2017)
Aluminum Nitride Thin Films Grown Sol-gel Spin Coating Technique.
In: 6th International Conference on Solid State Science & Technology and Workshop on Advanced Materials Technology: Growth & Characterization.
Abstract
In this study, aluminum nitride (AIN) thin films were grown on p-type silicon (1 00) substrate by sol-gel spin coating method. Two types of ethanol-based precursors were prepared , namely, precursors with and without the aid of diethanolamine (DEA). The objective of this work is to investigate the effects of the DEA on the surface morphology, structural and optical properties of the deposited thin films. The coating films were undergone nitridation process under ammonia ambient at 1100 oc for 60 min The surface morphology and structural properties of the deposited AIN thin films were investigated by atomic force microscopy (AFM) and X-ray diffraction (XRD). The AFM results showed that the AIN thin films has uniform and smooth surface. XRD results revealed that both samples of the deposited AIN thin films have AIN (1 00) preferred orientation. In addition, the crystallinity of sample without the aid of DEA is higher compared with the sample with the aid of DEA. The optical properties of AIN thin films were investigated by Raman and UV-Vis spectroscopy. Raman results showed the present of E1(TO) peak at 670 em 1 for sample without DEA and no peak is observed for sample with the aid of DEA. It was observed from UV-vis reflectance spectra that both samples were having energy band gap at around 5 eV. Finally, all the results revealed that the present of DEA affects the properties of AIN thin films.
Actions (login required)
|
View Item |