The Uv-Shielding Property Of
Zr0.7ce0.3o2-Kaolinite/Exfoliated Kaolinite
Composites Prepared By Differentsynthesis
Methods.
PhD thesis, Universiti Sains Malaysia.
Abstract
Kaolinite was obtained by elutriation of tin slime, which was then exfoliated by
planetary ball milling with 40 wt. % of urea for 1, 3 and 5 hours. Then the kaolinite
and urea-treated kaolinite samples were characterized by using XRD, XRF, SEM,
FTIR, and BET. The characterization results of kaolinite and urea-treated kaolinite
samples for 1, 3 and 5 hours proved that kaolinite was successfully exfoliated by urea
treatment for 5 hours and the XRD result of kaolinite showed minor gibbsite and
muscovite as impurities. Composites of Zr0.7Ce0.3O2-kaolinite/exfoliated kaolinite
were prepared by three different in-situ synthesis methods and one solid mixing
method. The first in-situ synthesis method was a citric acid complexing method, with
and without NH3 added; the second in-situ synthesis method was a soft solution
chemical method; and the third in-situ synthesis method was a hydrothermal
treatment method with and without sodium oleate added. For the solid mixing
method, Zr0.7Ce0.3O2, which was prepared by the three different synthesis methods
such as a citric acid complexing method without NH3 added, a soft solution chemical
method and a hydrothermal treatment without sodium oleate added, was solid mixed
with kaolinite/exfoliated kaolinite using an agate mortar and pestle. The resulting
composites were characterized by using XRD, FESEM and UV-Vis.