Preparation Of In-Situ Carbides Reinforced Hybrid Copper-Based Composite By Mechanical Alloying And Its Characterization

Le , Minh Hai (2010) Preparation Of In-Situ Carbides Reinforced Hybrid Copper-Based Composite By Mechanical Alloying And Its Characterization. Masters thesis, Universiti Sains Malaysia.

[img]
Preview
PDF
Download (1MB) | Preview

Abstract

The goal of this research work is to investigate the feasibility of the synthesis of two distinct in-situ carbides (NbC and TiC) simultaneously in a copper matrix via mechanical alloying and powder metallurgy from elemental powders of Cu, Nb, Ti and graphite. Three mixtures of starting powders with compositions corresponding to Cu-10vol.%NbC-10vol.%TiC, Cu-15vol.%NbC-15vol.%TiC and Cu-20vol.%NbC- 20vol.%TiC were mechanical alloyed using a planetary ball mill for 5, 10, 20 and 30 hours. The as-milled powders then were cold pressed at compaction pressure in range of 500-1000 MPa and sintered in a vacuum sintering furnace for 1 hour at different temperatures from 700 to 1000oC

Item Type: Thesis (Masters)
Subjects: T Technology > TN Mining Engineering. Metallurgy > TN1-997 Mining engineering. Metallurgy
Divisions: Kampus Kejuruteraan (Engineering Campus) > Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral (School of Material & Mineral Resource Engineering) > Thesis
Depositing User: Mr Mohammad Harish Sabri
Date Deposited: 04 Oct 2018 03:04
Last Modified: 12 Apr 2019 05:26
URI: http://eprints.usm.my/id/eprint/42285

Actions (login required)

View Item View Item
Share