Styrene-Methyl Methacrylatemodified Natural Rubber From Deproteinized Natural Rubber Latex.

Abstract

Kajian ini adalah mengenai pempolimeran in situ stirena (S) dan metil metakrilat (MMA) getah asli terubahsuai stirena-metil metakrilat di dalam lateks getah asli ternyahprotein menggunakan ammonium persulfat (N2H8O8S2) untuk menghasilkan getah asli terubahsuai S-MMA (S-MMA-NR) pada darjah ubahsuai yang berbeza, 10, 20 dan 30 % berat dengan berat monomer stirena dan MMA yang digunakan adalah sama (50/50 berat/berat). The study reported here is concerned with the in situ polymerization of styrene (S) and methyl methacrylate (MMA) in deproteinized natural rubber latex using ammonium persulfate (N2H8O8S2) as initiator to obtain S-MMA-modified natural rubber (S-MMA-NR) at different degree of modification, 10, 20 and 30 wt% of equal amount of styrene and MMA monomer (50/50 w/w).