Development Of Zn-Mn02 Battery Using Chitosan-Znci2. Gel Polymer Electrolytes.

Abstract

This project is divided into two main sections, that is to produce solid polymer electrolyte (SPE) as a proton conductor (H+) and to fabricate polymeric solid-state protonic battery with configuration of zinc (Zn)/SPE/manganese (IV) oxide (Mn02)' 1.0 g of chitosan was dissolved in 100 ml of 1 % acetic acid solution. Projek ini dibahagikan kepada dua bahagian utama iaitu penghasilan elektrolit polimer pepejal (SPE) sebagai konduktor proton (H+) dan fabrikasi bateri proton keadaan pepejalpolimer dengan konfigurasi zink (Zn)/SPE/mangan dioksida (Mn02)' 1.0 g kitosan dilarutkan dalam 100 mllarutan asid asetik 1 %. Garam ammonium nitrat (NH4N03) dan bahan pemplastik etilena karbonat (EC) ditarnbahkan ke dalam larutan kitosan tersebut.