Synthesis Of Ultrafine Bao.7sro.3Ti03 By Mechanically Activating Process.

Abstract

The project 'Synthesis of Ultrafine Bao.7SrOJTiD3 by Mechanically Activating Process' was successfully completed early 2008. As reported in the technical report attached, the single phase BST was produced successfully at a relatively low temperature of 500oe, albeit the challenges encountered during the synthesis, one of which is the caking problem as well as melting of phase formed. The caking effect was due to the mechanical activation process, while the melting phase was a result of the low meting chemicals used.